球阀阀座用聚三氟氯乙烯密封环工艺与性能

选用两种不同降温方式探究压制成型工艺对球阀阀座用聚三氟氯乙烯（PCTFE）密封环密封性能的影响。低温试验结果表明,自然降温工艺成型的制品外表面在常温-低温循环工况下出现裂纹,而保压降温得到的制品则不出现上述问题。性能测试与表征分析结果表明,自然降温工艺成型的密封环PCTFE其内部会出现微裂纹等缺陷,导致其在低温测试后出现亚表面裂纹,造成密封失效。降温阶段保压操作可抑制材料成型阶段微裂纹缺陷的产生,避免材料在室温-低温循环工况下因内应力而产生裂纹缺陷。     

复合铣整体叶盘通道加工工艺规划分析

首先对开式整体叶盘通道几何特征进行分析,在宽度和深度上对通道加工空间进行计算,从轴向和径向进行切削加工性分析;通过偏置面求解及其延伸面求解,进而确定可加工区域;在对比分析各种铣削方法基础上,优选复合铣削数控刀具,明确通道复合铣加工方法以及流程,为后续开式整体叶盘通道加工工艺优化打下基础。     

齿轮槽头型新型标准件安装工艺与试验研究

航空制造领域大量采用了如螺栓连接的标准件连接,随着新型飞机性能的提高,长寿命、高疲劳强度和高振动环境等指标对标准件的使用提出了更高的要求.本文通过开展齿轮槽头型新型标准件安装工艺与试验研究,一方面确定了该型标准件安装力矩等关键工艺参数及对复合材料的适用性,为其装机和使用提供理论依据及数据支持;另一方面,也对开展新型标准件安装工艺与试验的研究方法进行了有益的探索,对逐步形成一套完善的试验方法规范具有很好的指导作用.     

基于碳纳米管薄膜的复合材料层间增韧

通过浮动催化化学气相沉积法制备连续碳纳米管薄膜，并将其原位沉积到单向碳纤维织物表面，手工铺层后借助真空辅助树脂传递模塑成型（VARTM）工艺制备碳纳米管-碳纤维/环氧树脂复合材料层压板，研究不同面密度的碳纳米管薄膜对层压板Ⅱ型层间断裂韧性的影响。结果表明，随着碳纳米管薄膜面密度的增加，层压板Ⅱ型层间断裂韧性先逐渐提高，当碳纳米管薄膜面密度为9.64 g/m²时，层压板Ⅱ型层间断裂韧性最佳，与原始层压板相比提高了94%。碳纳米管通过桥接树脂裂纹、从树脂中拔出等方式提高层间断裂韧性。当碳纳米管面密度超过临界值时，会引起树脂浸润困难，导致增韧效果降低。     

热塑性定型剂对干铺丝-RTM工艺及力学性能影响

为了研究热塑性定型剂的添加对干铺丝-树脂传递模塑（RTM）工艺的影响，采用PA-6作为热塑性定型剂，通过T-剥离确定定型剂的质量分数，结合试验和工艺仿真，研究了定型剂对预制体面内渗透率的影响，并对其充模过程进行工艺仿真和分析，在此基础上研究了定型剂对环氧复合材料制品层间性能及韧性的影响。渗透率试验和仿真结果表明:加入定型剂后，纤维预制体的沿纤维和垂直纤维的面内渗透率分别降低了55.5%和52.0%；工艺仿真结果与试验结果一致，不同渗透长度下的注胶时间偏差均小于10%。力学性能试验结果表明:加入热塑性定型剂可显著提升环氧树脂复合材料的韧性，Ⅰ型和Ⅱ型层间断裂韧性分别提高了89.3%和54.1%，冲击韧性提高了18.7%，复合材料的层间剪切强度降低了23.6%。      

低温磨料气射流加工PDMS实验研究

通过自研的低温磨料气射流加工装置进行低温磨料气射流加工聚二甲基硅氧烷(polydimethylsiloxane,PDMS)实验研究,分析了加工时间、加工距离、冲蚀角度和磨料粒径对冲蚀率、孔深和孔横截面形貌的影响。结果表明:随着加工时间的增加,冲蚀率先增大后减小,在第1阶段加工过程中,孔深与加工时间大致呈线性关系,增加加工时间还可使孔底部变平整;存在一个最佳加工距离使孔深最大,当加工距离大于最大加工距离时,孔深将随着加工距离的增加而急剧下降,孔的锥度随着加工距离的增大而增大;当冲蚀角度处于30°～60°之间时,冲蚀率最大,随着冲蚀角度的增加,孔的形状逐步由椭圆形变成圆形;存在一个最佳磨料粒径,使冲蚀率和孔深达到最大;当冲蚀角度小于90°时,低温磨料气射流加工PDMS材料去除机理为塑性去除和脆性去除的结合。     

进气道堵盖打开过程数值模拟

为获得整体式固冲发动机转级过程中进气道堵盖(包括入口堵盖与出口堵盖)打开过程的流动形态,建立了进气道二维模型,利用Fluent动网格技术和UDF方法,开展了进气道堵盖打开过程非稳态流场研究。结果表明,在入口堵盖打开前,进气道前端形成强烈的弓形激波;在入口打开、出口未开的过程中,沿进气道轴向各监测点压强呈现周期性变化,振荡频率为100 Hz左右,出口堵盖位置压强振荡幅值为0.53 MPa;在出口打开后,补燃室残余热量形成的压强峰导致进气道在短时间内无法起动,随着背压降低至小于进气道再起动反压,进气道完全起动。     

纺丝工艺对炭纤维缠绕复合材料强度转化率的影响

通过不同纺丝工艺的聚丙烯腈基炭纤维表面状态、NOL环及Φ150 mm容器的实验研究,分析了不同纺丝工艺对湿法缠绕复合材料聚丙烯腈基炭纤维强度转化率的影响。结果表明,干喷湿纺炭纤维比湿法纺丝Φ150 mm容器环向纤维强度转化率要高出11.9%~15.4%,湿法纺丝的炭纤维复合材料NOL环层间剪切强度要比干喷湿纺炭纤维复合材料高7.4~34.1 MPa。因此,干喷湿纺的炭纤维可应用于固体火箭发动机缠绕壳体、压力容器等主要承受拉伸应力的领域,可充分发挥其纤维强度;而湿法纺丝工艺制成的炭纤维与树脂基体结合紧密,利于载荷的传递,可应用于承受压缩剪切等复杂载荷的领域,从而发挥这两种纤维各自不同优势。     

Advances in fabrication of ceramic corundum abrasives based on sol–gel process

Corundum abrasives with good chemical stability can be fabricated into various free abrasives and bonded abrasive tools that are widely used in the precision machining of various parts. However, these abrasives cannot satisfy the machining requirements of difficult-to-machine materials with high hardness, high strength, and strong wearing resistance. Although superhard abrasives can machine the above-mentioned materials, their dressing and manufacturing costs are high. By contrast, ceramic corundum abrasives fabricated by sol–gel method is a cost-effective product between conventional and superhard abrasives. Ceramic corundum abrasives exhibit self-sharpening and high toughness. In this review, the optimization methods of ceramic corundum abrasive properties are introduced from three aspects: precursor synthesis, particle shaping, and sintering. Firstly, the functional mechanism of seeds and additives on the microstructural and mechanical properties of abrasives is analyzed. Specifically, seeds can reduce the phase transition temperature and improve fracture toughness. The grain size and uniformly dense structure can be controlled by applying an appropriate amount of multicomponent additives. Then, the urgent need of engineering application and machinability of special shape ceramic corundum abrasives is reviewed, and three methods of abrasive shaping are summarized. The micromold replication technique is highly advanced and can be used to prepare functional abrasives. Additionally, the influence of a new sintering method, namely, two-step sintering technique, on the microstructural and mechanical performance of ceramic corundum abrasives is summarized. Finally, the challenge and developmental trend of the optimization of ceramic corundum abrasives are prospected.     

耐高温异氰酸酯/ 环氧树脂固化历程与性能

以异氰酸酯为固化剂固化环氧树脂,通过比较不同固化条件下固化物结构的差异,研究了异氰酸酯与环氧树脂的反应历程;改变异氰酸酯/环氧树脂体系的化学计量比(I/E),采用FTIR/ATR、DSC、DMTA等研究了固化产物的结构与性能。结果表明,异氰酸酯与环氧树脂的固化历程随着温度的升高可分为三个阶段,第一阶段为异氰酸酯的三聚反应;第二阶段是一个复杂的过程,首先环氧树脂和异氰酸酯可反应生成嗯唑烷酮结构,通过嗯唑烷酮环扩链得到端畀氰酸酯基低聚物,可继续发生三聚反应;第三阶段为异氰脲酸酯与残余的环氧基团反应生成嗯唑烷酮结构,异氰脲酸酯六元环向噁唑烷酮五元环的转化是一个可逆的过程。不同的I/E比例可得到结构不同的固化物,不同的结构导致固化物性能的差异:当(I/E)=1.8时,综合力学性能良好,异氰酸酯/环氧树脂/玻璃纤维复合材料的弯曲强度、弯曲模量、层剪强度分别为652.53、33270.63和31.66MPa,优于甲基四氢苯酐/环氧树脂/玻璃纤维复合材料力学性能;当I/E=2.0时,固化物T_g达到了305℃,明显优于传统的环氧树脂固化体系。